Manganese ntụ ntụ / manganese flakes
Nkọwa ngwaahịa
Manganese ntụ ntụ bụ ntụ ntụ ojii nke nwere nnukwu njupụta na ike.Ọ bụ ihe dị mkpa nke ụlọ ọrụ mmepụta ihe, ma nwee ọtụtụ ngwa n'imepụta ngwaahịa eletrọnịkị dị ka batrị na ngwaọrụ eletrọnịkị.Flakes manganese bụ mpempe akwụkwọ dị mkpa nke nwere ike dị elu na ike siri ike, nke a na-ejikarị eme ígwè.N'ihi ike ya dị elu na nke siri ike, flakes manganese nwere ike imeziwanye ike nkwụsị na ike nke ígwè.Manganese ntụ ntụ na manganese flakes na-arụsi ọrụ ike na akụrụngwa kemịkalụ ma nwee ike meghachi omume na ihe dị iche iche.N'ụlọ ọrụ eletrọnịkị, a na-eji manganese ntụ ntụ na flakes manganese eme ihe n'ọtụtụ ebe n'ichepụta batrị na ngwaọrụ eletrọnịkị, dịka maka imepụta ihe cathode, electrolytes na ihe ndị ọzọ.
Nkọwapụta
| Ihe | HR-Mn-P | HR-Mn-F |
| Ụdị: | ntụ ntụ | flake/chips |
| Mn | > 99.7 | > 99.9 |
| C | 0.01 | 0.02 |
| S | 0.03 | 0.02 |
| P | 0.001 | 0,002 |
| Si | 0,002 | 0,004 |
| Se | 0,0003 | 0,006 |
| Fe | 0,006 | 0.01 |
| Nha | 40-325 nchara | Flake/chips |
| 60-325 nchara | ||
| 80-325 nchara | ||
| 100-325 ntupu |
| Manganese ntụ ntụ mejupụtara | |||||||
| Ọkwa | Ngwakọta kemịkalụ% | ||||||
| Mn | C | S | P | Si | Fe | Se | |
| > | Pekarịrị |
|
|
|
|
| |
| HR-MnA | 99.95 | 0.01 | 0.03 | 0.001 | 0,002 | 0,006 | 0,0003 |
| HR-MnB | 99.9 | 0.02 | 0.04 | 0,002 | 0,004 | 0.01 | 0.001 |
| HR-MnC | 99.88 | 0.02 | 0.02 | 0,002 | 0,004 | 0.01 | 0.06 |
| HR-MnD | 99.8 | 0.03 | 0.04 | 0,002 | 0.01 | 0.03 | 0.08 |
ngwa
mgbakwunye alloy ọcha
welding consumables
alloy siri ike
elu okpomọkụ alloy, wdg.
Usoro njikwa mma
Huarui nwere usoro njikwa mma siri ike.Anyị na-anwale ngwaahịa anyị mbụ mgbe anyị mechara mmepụta anyị, anyị na-anwalekwa ọzọ tupu nnyefe ọ bụla, ọbụna sample.Ma ọ bụrụ na ịchọrọ, anyị ga-achọ ịnakwere ndị ọzọ iji nwalee.N'ezie ọ bụrụ na-amasị gị, anyị nwere ike ịnye gị sample iji nwalee.
Sichuan Metallurgical Institute na Guangzhou Institute of Metal Research kwadoro ogo ngwaahịa anyị.Ogologo oge imekọ ihe ọnụ na ha nwere ike ịzọpụta ọtụtụ oge ule maka ndị ahịa.